Mg和Ni机械合金化过程中的显微组织演变-加州大学(美国)

2015-03-11 09:54 下载量：1

资料摘要

资料下载

This study investigates the microstructural evolution during mechanical alloying of Mg and Ni, and during subsequent heat treatments of SPEX milled powders. The milling was performed under an inert argon atmosphere, employing two different ball-to-powder ratios (BPR): 10:1 and 20:1. It was observed that a large number of defects were produced during the ?rst hours of milling. These defects led to the amorphi- zation of part of the system, and promoted an extensive re?nement of the microstructure as well. Later on, the formation of the Mg2Ni compound due to the crystallization of the amorphous phase was observed. The microstructural details showed us that a possible complete sequence of phase transformations during milling of pure Mg and Ni could be: Mgc +Nic →Mgnc +Nic →amorphous + Ninc +Mgnc →amorphous +Ninc +Mg2Ninc →Mg2Ninc, where c and nc stand for crystalline and nanocrystalline, respectively. On the other hand, subsequent heat treatments of the milled powder showed that the amorphous phase could also be transformed into Mg2Ni by heating. Finally, the knowledge of the evolution of the microstructure during milling and annealing were combined to propose an optimal processing route to ef?ciently obtain the Mg2Ni compound.

资料下载

文献贡献者

培安有限公司

钻石会员 | 第21年

查看全部资料