This product contains full area coverage ReSe2 monolayers on c-cut sapphire substrates. Sample size measures 1cm in size and the entire sample surface contains monolayer thick ReSe2 sheet. Synthesized full area coverage monolayer ReSe2 is highly crystalline, some regions also display significant crystalline anisotropy.
Sample Properties.
Sample size | 1cm x 1cm square shaped |
Substrate type | Sapphire c-cut (0001) |
Coverage | Full monolayer coverage |
Electrical properties | 1.45 eV Anisotropic Semiconductor (Indirect Bandgap) |
Crystal structure | Distorted Tetragonal Phase (1T’) |
Unit cell parameters | a = 0.656 nm, b = 0.672 nm, c = 0.674 nm, α = 91.74°, β = 105°, γ = 119° |
Production method | Atmospheric Pressure Chemical Vapor Deposition (APCVD) |
Characterization methods | Raman, angle resolved Raman spectroscopy, photoluminescence, absorption spectroscopy TEM, EDS |
Specifications 1) Identification. Full coverage 100% monolayer ReSe2 uniformly covered across c-cut sapphire 2) Physical dimensions. One centimeter in size. Larger sizes up to 2-inch wafer-scale available upon requests. 3) Smoothness. Atomically smooth surface with roughness < 0.15 nm. 4) Uniformity. Highly uniform surface morphology. ReSe2 monolayers uniformly cover across the sample. 5) Purity. 99.9995% purity as determined by nano-SIMS measurements 6) Reliability. Repeatable Raman and photoluminescence response 7) Crystallinity. High crystalline quality, Raman response, and photoluminescence emission comparable to single crystalline monolayer flakes. 8) Substrate. c-cut Sapphire but our research and development team can transfer ReSe2 monolayers onto variety of substrates including PET, quartz, and SiO2/Si without significant compromisation of material quality.
Supporting datasets [for 100% Full area ReSe2 monolayers on c-cut Sapphire]
Transmission electron images (TEM) and angle resolved Raman spectroscopy measurements acquired from CVD grown full area coverage ReSe2 monolayers on c-cut sapphire confirming crystalline anisotropy
Energy dispersive X-ray spectroscopy (EDX) characterization on CVD grown full area coverage monolayer ReSe2 on c-cut sapphire
Raman spectroscopy measurement confirm monolayer nature of the CVD grown samples. Differential reflectance measurements clearly show band gap at 1.45 eV for monolayer ReS2 consistent with the existing literature values. PL spectrum does not show any PL signal due to indirect band nature.
GO 氧化石墨烯 (Graphene Oxide)
Carboxyl Graphene 羧基石墨烯
Graphene Fluoride 氟化石墨烯
PMMA涂层/预处理石墨烯(进口)
PET基底石墨烯(进口) Graphene on PET
铜基石墨烯薄膜(5*5cm)
铜基石墨烯薄膜(10*10cm)
PET基底石墨烯薄膜(1*1cm)
硅基底石墨烯薄膜(1*1cm)
基于SiO2/Si晶片的双层CVD石墨烯薄膜(4片装)
基于SiO2/Si晶片的双层CVD石墨烯薄膜(8片装)
Monolayer Black Phosphorus Solution 单层黑磷溶液
PtSe2 二硒化铂晶体 (Platinum Diselenide)
白云母(1片装) MICA muscovite V1
白云母(5片装) MICA muscovite V1
详细地址
关注
拨打电话
留言咨询