• 满足 MIL-C-675C 的严重磨损要求

• 在 8 – 11.5µm 范围内的透射率 ≥90%

• 适合在恶劣环境下使用

• 此外还提供无镀膜 3-5 微米 BBAR 和 8 - 12 微米 BBAR 镀膜锗窗口片

通用规格

倒角:	Protective as needed
有效孔径 (%):	90
涂层规格:	AR: Ravg ≤0.5% @ 8000 - 12000nm
边缘:	Fine Ground
努氏硬度 (kg/mm2) :	780
平行度（弧分）:	<1
基底:	Germanium (Ge)
表面质量:	60-40
波长范围 (nm):	8000 - 12000
Coating Abrasion:	AR: Moderate, per MIL-C-48497A Paragraph 4.5.3.3 DLC: Severe, per MIL-C-675C Paragraph 4.5.10
Coating Adhesion:	AR: per MIL-C-48497A Paragraph 4.5.3.1 DLC: per MIL-M-13508C Paragraph 4.4.6
Coating Humidity:	AR: per MIL-C-48497A Paragraph 4.5.3.2 DLC: ≥24 Hours per MIL-C-675C paragraph 4.5.8
Coating Salt Solubility:	AR: N/A DLC: ≥24 Hours Immersion per MIL-C-675C paragraph 4.5.7
Coating Salt Spray:	AR: N/A ≥24 Hours per MIL-C-675C paragraph 4.5.9
Coating Solubility and Cleaning:	AR: per MIL-C-48497A Paragraph 4.5.4.2 DLC: N/A
Coating Temperature (°F):	AR: -80 to +160 per MIL-C-48497A Paragraph 4.5.4.1 DLC: -80 to +160 per MIL-M-13508C Paragraph 4.4.4
Coating Wiper Durability:	AR: N/A DLC: ≥5,000 Wipes of Sand/Slurry per TS-1888
注意 :	Arrow on substrate edge points towards DLC coated surface

产品介绍

TECHSPEC® 类金刚石 (DLC) 镀膜锗窗口片在设计时考虑到了耐用性。这些窗口片的一个表面上具有高效的宽带增透膜，另一个表面上具有特殊设计的 DLC 镀膜，因此具有出众的透射率和环境耐受力。DLC 镀膜表面经过精心设计，可耐受从 -80 到 +160°F 的温度周期变化、持续 24 小时的盐雾、24 小时的浸盐溶解，以及沙土和泥浆混合物中的 5,000 次刮水器擦拭。此外，TECHSPEC® DLC 镀膜镀锗窗口片满足 MIL-C-675C的严重磨损要求。

订购信息

Dia. (mm)	厚度 (mm)	涂层	产品编码
25.00 +0.0/-0.1	1.00 ±0.1	S1: DLC Coating S2: BBAR (8000-12000nm)	13-795
25.00 +0.0/-0.1	3.00 ±0.1	S1: DLC Coating S2: BBAR (8000-12000nm)	13-796
50.00 +0.0/-0.1	1.00 ±0.1	S1: DLC Coating S2: BBAR (8000-12000nm)	13-797
50.00 +0.0/-0.1	3.00 ±0.1	S1: DLC Coating S2: BBAR (8000-12000nm)	13-798
75.00 +0.0/-0.1	5.00 ±0.1	S1: DLC Coating S2: BBAR (8000-12000nm)	13-799
100.00 +0.0/-0.1	6.00 ±0.1	S1: DLC Coating S2: BBAR (8000-12000nm)	21-087

技术数据

供货周期：	两周
品牌：	爱特蒙特
货号：	13-795