供货周期: | 一周 |
品牌: | 爱特蒙特 |
石英波片(相位延迟片)
(1)?零级及多级波片
(2)?λ/4 和 λ/2 延迟性
(3)?安装于黑色阳极电镀铝框中
(4)?零级聚合物波片 另外也备有
石英波片(相位延迟片)备有多级及零级型号可供选择,适用各种应用。多级波片适合波长偏离波片设计波长少于 ±1% 的应用。对于偏离超过 ±1% 的应用,建议使用零级波片,这类波片具有更大的带宽,对温度变化较不敏感。为简化系统整合,快光轴在支架边缘标出。
延迟性 | 延迟性容差 | 设计波长 DWL (nm) | 有效孔径 CA(mm) | 直径 (mm) | 产品号 |
λ/4 | ±λ/200 | 266 | 8 | 12.7 | #85-017 |
λ/2 | ±λ/200 | 266 | 8 | 12.7 | #85-031 |
λ/4 | ±λ/200 | 355 | 8 | 12.7 | #85-018 |
λ/2 | ±λ/200 | 355 | 8 | 12.7 | #85-032 |
λ/4 | ±λ/200 | 405 | 8 | 12.7 | #85-019 |
λ/2 | ±λ/200 | 405 | 8 | 12.7 | #85-033 |
λ/4 | ±λ/200 | 488 | 8 | 12.7 | #85-020 |
λ/2 | ±λ/200 | 488 | 8 | 12.7 | #85-034 |
λ/4 | ±λ/200 | 514.5 | 8 | 12.7 | #85-021 |
λ/2 | ±λ/200 | 514.5 | 8 | 12.7 | #85-035 |
λ/4 | ±λ/200 | 532 | 8 | 12.7 | #85-022 |
λ/2 | ±λ/200 | 532 | 8 | 12.7 | #85-037 |
λ/4 | ±λ/200 | 632.8 | 8 | 12.7 | #85-023 |
λ/2 | ±λ/200 | 632.8 | 8 | 12.7 | #85-038 |
λ/4 | ±λ/200 | 670 | 8 | 12.7 | #85-024 |
λ/2 | ±λ/200 | 670 | 8 | 12.7 | #85-039 |
λ/4 | ±λ/200 | 780 | 8 | 12.7 | #85-025 |
λ/2 | ±λ/200 | 780 | 8 | 12.7 | #85-041 |
λ/4 | ±λ/200 | 800 | 8 | 12.7 | #85-026 |
λ/2 | ±λ/200 | 800 | 8 | 12.7 | #85-042 |
λ/4 | ±λ/200 | 830 | 8 | 12.7 | #85-027 |
λ/2 | ±λ/200 | 830 | 8 | 12.7 | #85-043 |
λ/4 | ±λ/200 | 980 | 8 | 12.7 | #85-028 |
λ/2 | ±λ/200 | 980 | 8 | 12.7 | #85-044 |
λ/4 | ±λ/200 | 1064 | 8 | 12.7 | #85-029 |
λ/2 | ±λ/200 | 1064 | 8 | 12.7 | #85-045 |
λ/4 | ±λ/200 | 1550 | 8 | 12.7 | #85-030 |
λ/2 | ±λ/200 | 1550 | 8 | 12.7 | #85-046 |
λ/4 | ±λ/200 | 266 | 8 | 12.7 | #85-068 |
λ/2 | ±λ/200 | 266 | 8 | 12.7 | #85-079 |
λ/4 | ±λ/200 | 355 | 8 | 12.7 | #85-072 |
λ/2 | ±λ/200 | 355 | 8 | 12.7 | #85-080 |
λ/4 | ±λ/200 | 405 | 8 | 12.7 | #85-073 |
λ/2 | ±λ/200 | 405 | 8 | 12.7 | #85-081 |
λ/4 | ±λ/200 | 488 | 8 | 12.7 | #85-074 |
λ/2 | ±λ/200 | 488 | 8 | 12.7 | #85-082 |
λ/4 | ±λ/200 | 514.5 | 8 | 12.7 | #85-075 |
λ/2 | ±λ/200 | 514.5 | 8 | 12.7 | #85-083 |
λ/4 | ±λ/200 | 532 | 8 | 12.7 | #85-076 |
λ/2 | ±λ/200 | 532 | 8 | 12.7 | #85-084 |
λ/4 | ±λ/200 | 632.8 | 8 | 12.7 | #85-077 |
λ/2 | ±λ/200 | 632.8 | 8 | 12.7 | #85-085 |
λ/4 | ±λ/200 | 1064 | 8 | 12.7 | #85-078 |
λ/2 | ±λ/200 | 1064 | 8 | 12.7 | #85-086 |
λ/4 | ±λ/200 | 266 | 15 | 25.4 | #48-485 |
λ/2 | ±λ/200 | 266 | 15 | 25.4 | #48-486 |
λ/2 | ±λ/300 | 302 | 15 | 25.4 | #35-132 |
λ/4 | ±λ/300 | 302 | 15 | 25.4 | #35-133 |
λ/4 | ±λ/200 | 355 | 15 | 25.4 | #46-548 |
λ/2 | ±λ/200 | 355 | 15 | 25.4 | #46-549 |
λ/4 | ±λ/200 | 405 | 15 | 25.4 | #83-927 |
λ/2 | ±λ/200 | 405 | 15 | 25.4 | #83-928 |
λ/4 | ±λ/200 | 488 | 15 | 25.4 | #46-550 |
λ/2 | ±λ/200 | 488 | 15 | 25.4 | #46-551 |
λ/4 | ±λ/200 | 514.5 | 15 | 25.4 | #43-692 |
λ/2 | ±λ/200 | 514.5 | 15 | 25.4 | #43-693 |
λ/4 | ±λ/200 | 532 | 15 | 25.4 | #43-696 |
λ/2 | ±λ/200 | 532 | 15 | 25.4 | #43-697 |
λ/4 | ±λ/200 | 632.8 | 15 | 25.4 | #43-700 |
λ/2 | ±λ/200 | 632.8 | 15 | 25.4 | #43-701 |
λ/4 | ±λ/200 | 670 | 15 | 25.4 | #46-552 |
λ/2 | ±λ/200 | 670 | 15 | 25.4 | #46-553 |
λ/4 | ±λ/200 | 780 | 15 | 25.4 | #46-410 |
λ/2 | ±λ/200 | 780 | 15 | 25.4 | #46-411 |
λ/4 | ±λ/200 | 800 | 15 | 25.4 | #46-554 |
λ/2 | ±λ/200 | 800 | 15 | 25.4 | #46-555 |
λ/4 | ±λ/200 | 830 | 15 | 25.4 | #46-412 |
λ/2 | ±λ/200 | 830 | 15 | 25.4 | #46-413 |
λ/4 | ±λ/200 | 980 | 15 | 25.4 | #46-556 |
λ/2 | ±λ/200 | 980 | 15 | 25.4 | #46-557 |
λ/4 | ±λ/200 | 1064 | 15 | 25.4 | #43-704 |
λ/2 | ±λ/200 | 1064 | 15 | 25.4 | #43-705 |
λ/4 | ±λ/200 | 1550 | 15 | 25.4 | #46-414 |
λ/2 | ±λ/200 | 1550 | 15 | 25.4 | #46-415 |
λ/4 | ±λ/200 | 266 | 15 | 25.4 | #48-471 |
λ/2 | ±λ/200 | 266 | 15 | 25.4 | #48-472 |
λ/4 | ±λ/200 | 355 | 15 | 25.4 | #48-473 |
λ/2 | ±λ/200 | 355 | 15 | 25.4 | #48-474 |
λ/4 | ±λ/200 | 405 | 15 | 25.4 | #83-923 |
λ/2 | ±λ/200 | 405 | 15 | 25.4 | #83-924 |
λ/4 | ±λ/200 | 488 | 15 | 25.4 | #48-475 |
λ/2 | ±λ/200 | 488 | 15 | 25.4 | #48-476 |
λ/4 | ±λ/200 | 514.5 | 15 | 25.4 | #43-690 |
λ/2 | ±λ/200 | 514.5 | 15 | 25.4 | #43-691 |
λ/4 | ±λ/200 | 532 | 15 | 25.4 | #43-694 |
λ/2 | ±λ/200 | 532 | 15 | 25.4 | #43-695 |
λ/4 | ±λ/200 | 632.8 | 15 | 25.4 | #43-698 |
λ/2 | ±λ/200 | 632.8 | 15 | 25.4 | #43-699 |
λ/4 | ±λ/200 | 1064 | 15 | 25.4 | #43-702 |
λ/2 | ±λ/200 | 1064 | 15 | 25.4 | #43-703 |
λ/4 | ±λ/200 | 266 | 23 | 30 | #65-897 |
λ/2 | ±λ/200 | 266 | 23 | 30 | #65-898 |
λ/4 | ±λ/200 | 355 | 23 | 30 | #65-899 |
λ/2 | ±λ/200 | 355 | 23 | 30 | #65-900 |
λ/4 | ±λ/200 | 405 | 23 | 30 | #83-929 |
λ/2 | ±λ/200 | 405 | 23 | 30 | #83-930 |
λ/4 | ±λ/200 | 488 | 23 | 30 | #65-901 |
λ/2 | ±λ/200 | 488 | 23 | 30 | #65-902 |
λ/4 | ±λ/200 | 514.5 | 23 | 30 | #48-487 |
λ/2 | ±λ/200 | 514.5 | 23 | 30 | #48-488 |
λ/4 | ±λ/200 | 532 | 23 | 30 | #48-489 |
λ/2 | ±λ/200 | 532 | 23 | 30 | #48-490 |
λ/4 | ±λ/200 | 632.8 | 23 | 30 | #48-491 |
λ/2 | ±λ/200 | 632.8 | 23 | 30 | #48-492 |
λ/4 | ±λ/200 | 670 | 23 | 30 | #65-903 |
λ/2 | ±λ/200 | 670 | 23 | 30 | #65-904 |
λ/4 | ±λ/200 | 780 | 23 | 30 | #48-493 |
λ/2 | ±λ/200 | 780 | 23 | 30 | #48-494 |
λ/4 | ±λ/200 | 800 | 23 | 30 | #65-905 |
λ/2 | ±λ/200 | 800 | 23 | 30 | #65-906 |
λ/4 | ±λ/200 | 830 | 23 | 30 | #65-907 |
λ/2 | ±λ/200 | 830 | 23 | 30 | #65-908 |
λ/4 | ±λ/200 | 980 | 23 | 30 | #65-909 |
λ/2 | ±λ/200 | 980 | 23 | 30 | #65-910 |
λ/4 | ±λ/200 | 1064 | 23 | 30 | #48-495 |
λ/2 | ±λ/200 | 1064 | 23 | 30 | #48-496 |
λ/4 | ±λ/200 | 1550 | 23 | 30 | #65-911 |
λ/2 | ±λ/200 | 1550 | 23 | 30 | #65-912 |
λ/4 | ±λ/200 | 266 | 23 | 30 | #65-913 |
λ/2 | ±λ/200 | 266 | 23 | 30 | #65-914 |
λ/4 | ±λ/200 | 355 | 23 | 30 | #65-915 |
λ/2 | ±λ/200 | 355 | 23 | 30 | #65-916 |
λ/4 | ±λ/200 | 405 | 23 | 30 | #83-925 |
λ/2 | ±λ/200 | 405 | 23 | 30 | #83-926 |
λ/4 | ±λ/200 | 488 | 23 | 30 | #65-917 |
λ/2 | ±λ/200 | 488 | 23 | 30 | #65-918 |
λ/4 | ±λ/200 | 514.5 | 23 | 30 | #48-477 |
λ/2 | ±λ/200 | 514.5 | 23 | 30 | #48-478 |
λ/4 | ±λ/200 | 532 | 23 | 30 | #48-479 |
λ/2 | ±λ/200 | 532 | 23 | 30 | #48-480 |
λ/4 | ±λ/200 | 632.8 | 23 | 30 | #48-481 |
λ/2 | ±λ/200 | 632.8 | 23 | 30 | #48-482 |
λ/4 | ±λ/200 | 1064 | 23 | 30 | #48-483 |
λ/2 | ±λ/200 | 1064 | 23 | 30 | #48-484 |
λ/4 | ±λ/200 | 355 | 34 | 50.8 | #85-047 |
λ/2 | ±λ/200 | 355 | 34 | 50.8 | #85-052 |
λ/4 | ±λ/200 | 532 | 34 | 50.8 | #85-048 |
λ/2 | ±λ/200 | 532 | 34 | 50.8 | #85-053 |
λ/4 | ±λ/200 | 632.8 | 34 | 50.8 | #85-049 |
λ/2 | ±λ/200 | 632.8 | 34 | 50.8 | #85-054 |
λ/4 | ±λ/200 | 800 | 34 | 50.8 | #85-050 |
λ/2 | ±λ/200 | 800 | 34 | 50.8 | #85-055 |
λ/4 | ±λ/200 | 1064 | 34 | 50.8 | #85-051 |
λ/2 | ±λ/200 | 1064 | 34 | 50.8 | #85-057 |
λ/4 | ±λ/200 | 355 | 46 | 76.2 | #85-058 |
λ/2 | ±λ/200 | 355 | 46 | 76.2 | #85-063 |
λ/4 | ±λ/200 | 532 | 46 | 76.2 | #85-059 |
λ/2 | ±λ/200 | 532 | 46 | 76.2 | #85-064 |
λ/4 | ±λ/200 | 632.8 | 46 | 76.2 | #85-060 |
λ/2 | ±λ/200 | 632.8 | 46 | 76.2 | #85-065 |
λ/4 | ±λ/200 | 800 | 46 | 76.2 | #85-061 |
λ/2 | ±λ/200 | 800 | 46 | 76.2 | #85-066 |
λ/4 | ±λ/200 | 1064 | 46 | 76.2 | #85-062 |
λ/2 | ±λ/200 | 1064 | 46 | 76.2 | #85-067 |
订购信息:
12.7mm Dia. 266nm λ/4 Quartz Waveplate Zero Order
库存#85-017技术参数与相关资料
类型 | Zero Order Waveplate |
延迟性 | λ/4 |
延迟性容差 | ±λ/200 |
设计波长 DWL (nm) | 266 |
直径 (mm) | 12.7 |
防护罩容差 (mm) | +0/-0.25 |
有效孔径 CA(mm) | 8 |
厚度 (mm) | 6.4 |
表面平整度 | λ/10 |
表面质量 | 10-5 |
平行度(弧秒) | 0.5 |
基底 | Crystal Quartz |
涂层 | Laser V-Coat |
涂层规格 | Rabs <0.25% @ 266nm |
Damage Threshold, Pulsed | 3.5 @ 1064nm J/cm2 @ 10ns |
温度系数 (λ/°C) | 0.0001 |
构造 | Crystalline |
RoHS | 符合标准 |
12.7mm Dia. 266nm λ/2 Quartz Waveplate Zero Order
库存#85-031技术参数与相关资料
类型 | Zero Order Waveplate |
延迟性 | λ/2 |
延迟性容差 | ±λ/200 |
设计波长 DWL (nm) | 266 |
直径 (mm) | 12.7 |
防护罩容差 (mm) | +0/-0.25 |
有效孔径 CA(mm) | 8 |
厚度 (mm) | 6.4 |
表面平整度 | λ/10 |
表面质量 | 10-5 |
平行度(弧秒) | 0.5 |
基底 | Crystal Quartz |
涂层 | Laser V-Coat |
涂层规格 | Rabs <0.25% @ 266nm |
Damage Threshold, Pulsed | 3.5 @ 1064nm J/cm2 @ 10ns |
温度系数 (λ/°C) | 0.0001 |
构造 | Crystalline |
RoHS | 符合标准 |
25.4mm Dia. 266nm λ/4 Quartz Waveplate Zero Order
库存#48-485技术参数与相关资料
类型 | Zero Order Waveplate |
延迟性 | λ/4 |
延迟性容差 | ±λ/200 |
设计波长 DWL (nm) | 266 |
直径 (mm) | 25.4 |
防护罩容差 (mm) | +0/-0.25 |
有效孔径 CA(mm) | 15 |
厚度 (mm) | 7.8 |
表面平整度 | λ/10 |
表面质量 | 10-5 |
平行度(弧秒) | 0.5 |
基底 | Crystal Quartz |
涂层 | Laser V-Coat |
涂层规格 | Rabs <0.25% @ 266nm |
Damage Threshold, Pulsed | 3.5 @ 1064nm J/cm2 @ 10ns |
温度系数 (λ/°C) | 0.0001 |
构造 | Crystalline |
RoHS | 符合标准 |
25.4mm Dia. 266nm λ/2 Quartz Waveplate Zero Order
库存#48-486技术参数与相关资料
类型 | Zero Order Waveplate |
延迟性 | λ/2 |
延迟性容差 | ±λ/200 |
设计波长 DWL (nm) | 266 |
直径 (mm) | 25.4 |
防护罩容差 (mm) | +0/-0.25 |
有效孔径 CA(mm) | 15 |
厚度 (mm) | 7.8 |
表面平整度 | λ/10 |
表面质量 | 10-5 |
平行度(弧秒) | 0.5 |
基底 | Crystal Quartz |
涂层 | Laser V-Coat |
涂层规格 | Rabs <0.25% @ 266nm |
Damage Threshold, Pulsed | 3.5 @ 1064nm J/cm2 @ 10ns |
温度系数 (λ/°C) | 0.0001 |
构造 | Crystalline |
RoHS | 符合标准 |
30mm Dia. 266nm λ/4 Quartz Waveplate Zero Order
库存#65-897技术参数与相关资料
类型 | Zero Order Waveplate |
延迟性 | λ/4 |
延迟性容差 | ±λ/200 |
设计波长 DWL (nm) | 266 |
直径 (mm) | 30.0 |
防护罩容差 (mm) | +0/-0.25 |
有效孔径 CA(mm) | 23.0 |
厚度 (mm) | 6.0 |
表面平整度 | λ/10 |
表面质量 | 10-5 |
平行度(弧秒) | 0.5 |
基底 | Crystal Quartz |
涂层 | Laser V-Coat |
涂层规格 | Rabs <0.25% @ 266nm |
Damage Threshold, Pulsed | 3.5 @ 1064nm J/cm2 @ 10ns |
温度系数 (λ/°C) | 0.0001 |
构造 | Crystalline |
RoHS | 符合标准 |
30mm Dia. 266nm λ/2 Quartz Waveplate Zero Order
库存#65-898技术参数与相关资料
类型 | Zero Order Waveplate |
延迟性 | λ/2 |
延迟性容差 | ±λ/200 |
设计波长 DWL (nm) | 266 |
直径 (mm) | 30.0 |
防护罩容差 (mm) | +0/-0.25 |
有效孔径 CA(mm) | 23.0 |
厚度 (mm) | 6.0 |
表面平整度 | λ/10 |
表面质量 | 10-5 |
平行度(弧秒) | 0.5 |
基底 | Crystal Quartz |
涂层 | Laser V-Coat |
涂层规格 | Rabs <0.25% @ 266nm |
Damage Threshold, Pulsed | 3.5 @ 1064nm J/cm2 @ 10ns |
温度系数 (λ/°C) | 0.0001 |
构造 | Crystalline |
RoHS | 符合标准 |