色谱氧化铝填充柱

标准:GB/T-6609.31-2009 Chemical analysis methods and determination of physical performance of alumina - Part 31: Determination of angle of flostandard: GB/T-6609.31-2009 Chemical analysis methods and determination of physical performance of alumina-Part 31: Determination of angle of flo 适用范围:本部分适用于氧化铝流动角测定，测定范围：30°-50°.Scope of application:This part is applicable to the determination of alumina flow angle, the measurement range: 30°-50°. 流动角：试料在测试瓶中停止流动后，试料形成的椎形面与测试瓶底间形成的角度。Flow angle:The angle formed between the conical surface formed by the sample and the bottom of the test bottle after the sample stops flowing in the test bottle. 原理：将氧化铝通过一系列漏斗倒入平底容器中。允许通过漏口下漏的氧化铝流出平底容器，根据用于填充容器的试料质量和试验后容器内存在试料的质量计算流动角度.principle:Pour the alumina through a series of funnels into a flat-bottomed container. Allow the alumina leaking through the leak to flow out of the flat-bottomed container, and calculate the flow angle based on the mass of the sample used to fill the container and the mass of the sample in the container after the test. 技术参数:1.漏斗：直径为110mm±10mm，内部瓶颈的直径为10mm±2mm2.不锈钢可调节流速漏斗：壁内光滑的金属漏斗，直径为65mm±5mm；内部瓶颈的直径为5.5mm±0.5mm，长度为110mm±20mm。漏斗瓶颈的长度为50mm±5mm，瓶颈底部终止处为正方形.3.平底容器：内径为72.5mm±0.1mm，内高为72.5mm±0.1mm，漏口的直径是4mm±0.1mm，漏口的壁和根部的厚度为4.5mm±0.1mm，容器的理论容积为300mL，此容器为铝质，内壁光滑，表面平坦.4.孔塞：孔塞的尺寸能够塞紧平底容器底部漏口5.塑料杯：容积约为400ml6.称重天平客户自备7.钢尺,毛刷.溢出接料盘.Technical Parameters:1. Funnel: the diameter is 110mm±10mm, the diameter of the inner bottleneck is 10mm±2mm2. Stainless steel adjustable flow rate funnel:A smooth metal funnel with a diameter of 65mm±5mm The diameter of the internal bottleneck is 5.5mm±0.5mm and the length is 110mm±20mm.The length of the bottleneck of the funnel is 50mm±5mm, and the end of the bottom of the bottleneck is square.3. Flat-bottomed container: the inner diameter is 72.5mm±0.1mm, the inner height is 72.5mm±0.1mm, the diameter of the drain is 4mm±0.1mm, the thickness of the wall and root of the drain is 4.5mm±0.1mm, the theory of the container The volume is 300mL. This container is made of aluminum, with a smooth inner wall and a flat surface.4. Hole plug: The size of the hole plug can close the bottom leak of the flat-bottomed container5. Plastic cup: the volume is about 400ml6. The weighing balance is provided by the customer7. Steel ruler, brush. Overflow receiving tray.

氧化铝粉末流动性角测试仪ZK660931XZK660931氧化铝流动角测定仪 适用范围:本部分适用于氧化铝流动角测定，测定范围：30°-50°.流动角：试料在测试瓶中停止流动后，试料形成的椎形面与测试瓶底间形成的角度。原理：将氧化铝通过一系列漏斗倒入平底容器中。允许通过漏口下漏的氧化铝流出平底容器，根据用于填充容器的试料质量和试验后容器内存在试料的质量计算流动角度.技术参数:1.漏斗：直径为110mm±10mm，内部瓶颈的直径为10mm±2mm2.不锈钢可调节流速漏斗：壁内光滑的金属漏斗，直径为65mm±5mm；内部瓶颈的直径为5.5mm±0.5mm，长度为110mm±20mm。漏斗瓶颈的长度为50mm±5mm，瓶颈底部终止处为正方形.3.平底容器：内径为72.5mm±0.1mm，内高为72.5mm±0.1mm，漏口的直径是4mm±0.1mm，漏口的壁和根部的厚度为4.5mm±0.1mm，容器的理论容积为300mL，此容器为铝质，内壁光滑，表面平坦.4.孔塞：孔塞的尺寸能够塞紧平底容器底部漏口5.塑料杯：容积约为400ml6.称重天平客户自备7.钢尺,毛刷.溢出接料盘.

该膜为无机膜，由一种特殊形式的非晶氧化铝膜构成，这种膜具有均匀分布的纳米孔结构，其厚度、孔径、孔间距、孔隙率等均高度可控。 相较与有机过滤薄膜，它的优点很多，包括: 1、超高流通量，由于其极高的孔密度和孔隙率，使得孔径这么小的滤膜具有前所未有的高流通量，使得它在短时间内能达到想要的过滤效果。 2、孔径在孔径大小可控的过滤介质中最小，可达到10纳米（经过处理可进一步减小），并且不存在两个，三个或更多的孔的组合体。 3、超高效的颗粒保留能力，颗粒在膜表面被筛分，而不是在膜孔内某处。 4、为细胞的附着和生长提供刚性、均匀的表面，并且由于潮湿时几乎透明，使得光学显微镜较易观察到细胞的成长。(潮湿时折射指数为1.60 +/- 0.01)。 5、不保留背景污点，因此适用于包括荧光和免疫荧光的各种着色技术。 6、在要求干扰最小的精细试验中是最低水平的可提取材料。 7、耐高温（在摄氏1000度以下膜结构稳定）和抗辐射。 8、 对于SEM检测是理想的射线稳定底层。 9、高的化学相容性 应用领域&mdash &mdash 1、作为滤膜，适用于非常广范围的专业研究中，比如： * 高性能液相色谱（HPLC）中移动相的过滤和去气。 * 外荧光光学显微镜下的细菌分析。 * 溶剂的极度清洁。 * 重量分析和脂质体挤压的研究。 * 筛一样的结构使得留在膜表面的微生物和微粒可以在电子显微镜下进行观察。我们一般认为，是氧化铝膜的耐高温或可用作强性介质的特性让人们想到用它, 但事实上，它的透明特征才是这一系列膜产品大量销售的原因。 * 无需移动保留下来的物质就可直接用光学显微镜进行观察（移动很容易造成样本损失），这是由于膜在潮湿时呈透明状。 2、可作为电子束和离子束曝光，或者反应离子刻蚀等的掩模板，制作纳米点阵结构。 3、可作为滤光片，这是由于其具有一定程度上的光子晶体结构。 目前可提供厚度50微米，孔径30-70纳米，面积几平方厘米的膜，但从技术上来说，完全具备各种规格（厚度2微米到200微米，孔径10-200纳米，面积从几平方毫米到几十平方厘米）的氧化铝过滤膜制备能力，只是我们的交货时间要视客户对膜的具体要求而定，有些制备难度较高、工艺较复杂的膜的交货时间要适当延长。