每周分享：An acid-free route for the facile synthesis of iron-functionalized mesoporous silicas: Transformation between hollow nanospheres and cage-like mesostructures

今天给大家分享的是2014年5月份《Microporous and Mesoporous Materials》上发表的一篇名为：An acid-free route for the facile synthesis of iron-functionalized mesoporous silicas: Transformation between hollow nanospheres and cage-like mesostructures

文章摘要如下：

Iron-substituted silicas with hollow nanospherical morphology and cage-like mesostructure have been synthesized using triblock copolymer F127 as surfactant and tetramethoxysilane (TMOS) as silica source with no necessary addition of mineral acids. Iron-functionalized hollow nanospheres were obtained using Fe(acac)3 as iron source. When Fe(NO3)3 was employed as iron source, iron-containing cage-like FDU-12 mesostructure and hollow nanospheres were formed with Fe/Si molar ratio lower than 0.008 and higher than 0.015, respectively. The formation of hollow spheres at high Fe/Si ratio can be regarded as gradually dissociation of nanocages from Fe-FDU-12. The structure of the iron centers was determined by spectroscopic methods (UV–vis and UV–Raman measurements) and by elemental analyses. The facile structural evolution between cage-like and nanospherical structures may be helpful for further understanding the formation mechanism of mesoporous silicas.

该文章中材料表征采用的是美国麦克仪器AutoChem 2920

详情可参考下面链接：

http://www.sciencedirect.com/science/article/pii/S1387181114000456

阅读133次

关注

上一篇麦克仪器祝您新春快乐

下一篇每周分享