Characterization and corrosion studies of titania-coated NiTi prepared by sol–gel technique and steam crystallization

2014/09/04   下载量： 4 次

方案摘要

方案下载
应用领域
检测样本
检测项目
参考标准

Nickel titanium (NiTi) was dip-coated with titania via the sol–gel route using titanium butoxide (Ti(OC4H9)4) as precursor. The as-coated titania film was crystallized to form anatase by treatment in steam at 1058C. The crystallized film was relatively thick (about 750 nm) and even. Atomic force microscopy (AFM) revealed that the film was dense with a surface roughness of about 3 nm, and was composed of particles of about 100 nm. X-ray diffractometry (XRD) showed that these particles were composed of nanocrystallites of a few nanometers.

方案下载
上一篇 普林斯顿及输力强：恒电量瞬态扰动测量Tafel 斜率及数据积分处理
下一篇 The Use of Conducting Polyaniline as Corrosion Inhibitor for Mild Steel in Hydrochloric Acid

文献贡献者

阿美特克科学仪器部（普林斯顿及输力强）
银牌会员 丨 第20年
查看全部资料
相关仪器 更多
相关方案
更多

相关产品

当前位置： 普林斯顿及输力强 方案 Characterization and corrosion studies of titania-coated NiTi prepared by sol–gel technique and steam crystallization

关注

拨打电话

留言咨询