Raman image (Figure 1) from a thin film of azobenzene-containing polymer thin film (300 nm) that is periodically structured (periodicity of ~1 µm). Raman measurements were recorded with a Labram HR 800 (HORIBA JobinYvon) spectrometer combined with an inverted microscope (Olympus IX 71) and a X,Y Piezoelectric stage to position the sample with the best accuracy and repeatability. A 100X, 0.9 NA microscope objective was used. A Raman spectrum (Fig. 2) was recorded every 100 nm along the X and Y directions with an integration time of 5 seconds per spectrum (λ excitation=752.4 nm). The variation of the Raman signal was integrated over the [10601180]cm-1 spectral domain (Figure 3). It must pointed out that details on the Raman profile are obtained with a spatial resolution better than λ/2 (at the diffraction limit).
Raman image (Figure 1) from a thin film of azobenzene-containing polymer thin film (300 nm) that is periodically structured (periodicity of ~1 µm). Raman measurements were recorded with a Labram HR 800 (HORIBA JobinYvon) spectrometer combined with an inverted microscope (Olympus IX 71) and a X,Y Piezoelectric stage to position the sample with the best accuracy and repeatability. A 100X, 0.9 NA microscope objective was used. A Raman spectrum (Fig. 2) was recorded every 100 nm along the X and Y directions with an integration time of 5 seconds per spectrum (λ excitation=752.4 nm). The variation of the Raman signal was integrated over the [10601180]cm-1 spectral domain (Figure 3). It must pointed out that details on the Raman profile are obtained with a spatial resolution better than λ/2 (at the diffraction limit).
颗粒分析+混合氧化石墨烯+分散状态的混合比例
颗粒分析+聚苯乙烯乳胶混合样品+粒径分布
颗粒分析+二氧化硅+CMP浆料质量控制
相关产品
HORIBA XploRA Nano原子力-拉曼联用系统
HORIBA高灵敏一体式FluoroMax-4荧光光谱仪
HORIBA Fluorolog®-3科研级荧光光谱仪
HORIBA XploRA INV多功能拉曼及成像光谱仪
HORIBA EMGA-Expert 氧氮氢分析仪
HORIBA EMGA-Pro氧氮氢分析仪
HORIBA 离心式粒度分析仪Partica CENTRIFUGE CN-300
HORIBA Fluorolog-QM模块化科研级稳瞬态荧光光谱仪
ViewSizer 3000 纳米颗粒追踪分析仪
HORIBA LabRAM Odyssey 高速高分辨显微共焦拉曼光谱仪
HORIBA LabRAM Soleil™高分辨超灵敏智能拉曼成像仪
HORIBA NANO Raman
HORIBA XGT-9000 X射线显微分析仪
HORIBA Duetta荧光及吸收光谱仪
HORIBA MacroRAM 台式一体化拉曼光谱仪
关注
拨打电话
留言咨询