采用LaVision公司的形变应变测量系统StrainMaster,对骨盆模型在外力下的变形和应变及裂纹生成机制进行了实验测量研究。
With a growing elderly population, osteoporotic pelvic fractures have been an increasingly common worldwide problem. Due to the complexity of the human pelvis, difficulties exist in the diagnosis of subtle fractures and complications may arise from standard treatments. Guidelines for approaching pelvic fracture have been established, but the uniqueness and complexity of the pelvis leaves much to professional discretion. This thesis showed how a biomechanical study provides more objective insights in dealing with the pelvic fractures.
A three-dimensional digital image correlation (3D-DIC) was used for its ability to extract mechanical measurements across a sizeable area of the contoured pelvic surface. From a preliminary study, a procedure was established to effectively conduct an optimized experiment with this technique and to quantify the uncertainty of its measurements. An existing experimental setup was redesigned and reconfigured for testing and measuring with an integrated DIC system. From initial experimentation and validation, it was shown that crack behavior can be accurately characterized using the ability of the test setup to measure crack edge openings as small as 0.03 mm with less than 10% uncertainty.
When testing on an intact pelvis, the measurements were very repeatable, observed to be about 10% for strain measurements. After testing a fractured pelvis and comparing the results to the intact pelvis, it could be seen how a crack causes shifts in the tension and compression profiles experienced by a normal pelvis. It was also shown that the test setup could observe crack behavior on a microscopic scale while observing a significant area of the pelvis. Crack edge opening measurements with less than 10% uncertainty were then used to characterize the stability of the fractured specimen. The designed setup was proven to be an effective tool for analyzing the mechanics and stability of a fractured pelvis.
在一个双稳湍流涡旋火焰中,对间歇性动态的时间-频率定位
Particle-laden Taylor-Couette流:高阶转变和径向局部波浪涡旋的证据
7根杆束的流体-结构相互作用:用实验数据对比数值模拟
相关产品
汽车光学检测系统AIS
PT403型波长可调谐皮秒激光器
ANL系列高能量高重复频率DPSS纳秒激光器
APL4206 系列高能量皮秒激光放大器
UltraFlux FF/FT 5000 高能量可调谐飞秒激光器系统
UltraFlux FT300型波长可调谐飞秒激光器系统
Ekspla 超高功率激光器系统SYLOS 2A
LaVision PTUx 可编程时间控制单元
LaVision 用于粒子成像测速PIV的相机
LaVision StrainMaser 全场应变测试系统组件
LaVision 用于数字图像相关DIC的相机
LaVision StrainMaster 数字图像相关分析软件包
LaVision 标定板
LaVision StrainMaster 形变应变成像测量系统
LaVision StrainMaster DVC 体视全场应变测量系统
关注
拨打电话
留言咨询