大陆
第1楼2008/10/27
Peak list:(Cu alpha diffraction 1.5406Angs.)
No. 2Theta,deg. d-spacing,Angs. Int. F h k l Mult.
1 28.548 3.1242 4508727.79 193.61 1 1 1 8
2 33.083 2.7056 1203279.14 135.32 0 0 2 6
3 47.486 1.9131 2536643.56 207.53 0 2 2 12
4 56.345 1.6315 2001675.47 158.35 1 1 3 24
5 59.092 1.5621 368889.07 124.24 2 2 2 8
6 69.418 1.3528 372964.49 171.73 0 0 4 6
7 76.706 1.2414 813406.54 139.42 1 3 3 24
8 79.081 1.2100 523273.20 114.70 0 2 4 24
9 88.435 1.1046 792572.84 151.67 2 2 4 24
Ref. Info.:
'Journal of Solid State Chemistry', 147, 485-500(1999)
'Kuemmerle, E.A.'
'Heger, G.'
a 5.4112(10)
b 5.4112(10)
c 5.4112(10)
alpha 90.
beta 90.
gamma 90.
volume 158.45
formula_units_Z 4
space_group_name_H-M 'F m -3 m'
Int_Tables_number 225
R_factor_all .008
Temperature: R.T. ~ 300K