The long-period stacking order (LPSO) structures in rapidly solidified Mg97Zn1Y2 alloy have been studied by conventional and highresolution
transmission electron microscopes (HRTEMs). There are four kinds of stacking sequences in the LPSO structures, i.e., 18R of
ABABABCACACABCBCBC, 14H ofACBCBABABABCBC, 10H ofABACBCBCABand 24R ofABABABABCACACACABCBCBCBC.
The 18R structure is dominantly observed in the present study. The rest three are occasionally observed in places. The 10H and 24R structures
are recently discovered. The lattice constants of 18R(1 -1 1 -1 2)3, 14H(-2 1 -2 1 -1 1 -1 2-1 2), 10H(1 -3 1 -1 3 -1) and 24R(1 -1 1 -1 1 -1 2)3 structures are
estimated to be a = 0.320 nm and c = 4.678 nm, a = 0.325 nm and c = 3.694 nm, a = 0.325 nm and c = 2.603 nm, a = 0.322 nm and c = 6.181 nm
for the hexagonal structure, respectively
不知道在我这张图中怎么去标a,c的值