如何确定 位错线方向

应助达人

不太明白这个图，应该只是表面位错方向吧

应助达人

根据衍射图标定晶面和晶带轴，然后对应到实空间的晶面，垂直于晶面的就是晶向，即图中标示的指数

不知道你这个是否是双束明场像，如果是双束条件拍的，箭头对应的就是相应的g矢量，当然，如果不是双束条件，那就是二楼说的方法

倒腾一下，其实正空间晶向就对应倒空间衍射点的方向，因为衍射点与透射点的连线与晶面垂直，晶向与晶面垂直。但我有这个疑问，这一方法适合所有晶系吗？还是只是立方晶系？

这是一文献，Microstructure-based analysis of fatigue behaviour of Al-Si-Mg alloy 。 相关内容就是：
From the dislocation structures, [011] crystallographic axis of dislocation structure is fairly
clear. Two typical slip-lines are observed, the directions are [211] or [211] and the cross-slip angle is 70.6?.
This can prove that the movement of dislocation structure has a certain regularity during the process. From these results, it is found that slip systems are activated through the process, and the slip line starts and bears a lot of plastic deformation. With other factors such as pile up of dislocations against boundaries, the energy for further movement is greater than the needed, then another set of slip systems starts and begins to develop cross-banded sliding structure, some other slip systems may be also activated later. 看图片也不是严格双束条件。我就是不懂图中箭头方向【-211】如何定的？

不管是不是双束条件，都是根据衍射点定的方向

应助达人

图中剪头方向只是衍射矢量的方向，并不是位错线方向

应助达人

额，好像说错了(ノ???Δ??? )ノ

应助达人

严格来说，也对！因为空间中位错线方向的确定还要稍微复杂一些！这个直接这样标，如果硬要说是位错线方向，还是不够严格！